英语释义

1. a mineral 5CaSiO3?H2O that is a hydrous calcium silicate

片语

ultra-light xonotlite超轻硬硅钙石

xonotlite insulation materials硬硅钙石绝热材料

xonotlite fibrous particle硬硅钙纤维粒子

xonotlite-type硬硅钙石型

xonotlite secondary particles硬硅钙石二次粒子

xonotlite secondary particle硬硅钙石二次粒子

eakleite硬硅钙石

super-light xonotlite超轻硬硅钙石制品

xonotlite fiber硬硅钙石纤维

英汉例句

• Xonotlite-based material is a very useful insulation material, because spherical xonotlite agglomerates which are synthesized with dynamic hydrothermal rrocess consist of many pores.

  通过动态水热法合成出的球形硬硅钙石颗粒具有很高的气孔率，使轻制硬硅钙石材料成为一种用途广泛的绝热（保温）材料。

• The results were as follows: the needle crystal of xonotlite was controlled by reaction temperature, pressure and time.

  认为 ：硬硅钙石针状晶体是平衡反应的最终产物 ，在适当的温度、压力下 ，经过一定的反应时间就能生成。

• Lime with high activity should be utilized as calcareous material to produce super-light xonotlite and the activity of siliceous material should match that of calcareous material.

  制备超轻硬硅钙石制品必须使用高活性的石灰作为钙质原料，而所使用的硅质原料活性应与之相匹配。

• However, hollow structure is harm to the study on the properties and applications of ultrafine xonotlite fibers.

  然而，半中空球对进一步深入研究超细直径硬硅钙石纤维的性能与应用造成很大的局限。

• The formation of hollow secondary particles of xonotlite was controlled by kinetics. The dissolution speed of quartz is important in forming hollow secondary particles of xonotlite.

  而中空二次粒子球的形成则是一个动力学控制过程，在整个成球反应过程中，石英粉的溶解速度是关键。

• The results indicate that stirring evidently affects the formation and morphology of xonotlite secondary particles, and further affects the dry shrinkage and bulk density of xonotlite products.

  结果表明，搅拌对上述性质的影响非常显着，并且进一步影响硬硅钙石制品的干燥收缩率及体积密度。

• Several silica raw materials with very different nature were used to produce xonotlite secondary particles.

  几种硅质原料被用于硬硅钙石二次粒子制备中。

• Ultra_light calcium silicate insulation material is constructed with spherical agglomerates of fibrous xonotlite crystals.

  超轻硅酸钙材料实际上是由硬硅钙石纤维状晶体组成的多孔球状团聚体构成。

• The secondary particle sphere of xonotlite yielded by konilite is of hollow structure, however, for the carbon white fibrous crystal just stacked densely and balling up is poor.

  由粉石英制备的硬硅钙石二次粒子球具有中空结构，而白炭黑对应样品则以纤维聚集成的块体为主，成球差。