片语

mold temperature distribution模具温度分布

mold clearing temperature出模温度

Mold surface temperature模具表面温度

mold cavity temperature模腔表面温度

mold filling temperature充型温度

mold temperature detail铸模温度

mold temperature control device模具温控装置

dynamic mold surface temperature动态模面温度

英汉例句

• effects of different cooling rates and uneven mold temperature on the residual stress inside injection molded parts are studied with the help of numerical methods.

  采用数值方法研究了不同冷却速率、不均匀模壁温度对塑件残余应力的影响。

• the mold temperature is controlled effectively by controlling the flow of the external coolant through the heat exchanger.

  具温度是有效的控制，通过控制流通的外部冷却水通过换热器。

• proper decrease in pouring temperature and increase in shell mold temperature are helpful to preventing hot tear.

  为避免产生热裂应适当降低浇注温度，提高型壳温度。

• with this evaporative cooling approach, the mold temperature is automatically evened out.

  与此蒸发冷却的方法，具温度是自动，最终列。

• large parts of the workpiece wall thick liquid aluminum solidification slow, mold temperature can be somewhat less;

  工件壁厚较大部位的铝液凝固慢，模温可稍低些；

• the control of mold temperature in injecting process has extraordinary important influences not only on the quality of the injected products but also on the process itself.

  注塑模具的温度控制对注塑工艺和注塑件的质量有非常重要的影响。

• this evaporative cooling approach to mold temperature control provides an excellent general solution to the problem of achieving uniform mold temperature and precise control.

  这蒸发者冷却的接近形成温度控制提供优良的达成统一的子温度和精确的控制的问题的一般解决办法。

• before using, it should be dried in vacuum drier at 120-130℃. control mold temperature at 60-90℃. injecting adopted low temperature, middle speed and high pressure.

  使用前在真空烘箱中120-130℃烘干3小时以上，模具温度控制在60-90℃。注射成型采用低温、高速、高压的方法。

• the results showed that the products would get the best mechanical performance while the fiber content was 30% and the mold temperature was 50℃ , which was verified in the actual production.

  结果表明，当玻纤质量分数为30％、模具温度为50％时，复合材料表现出优良的力学性能，这一结果在实际生产中也得到了验证。

• the effects of casting speed and water flowrate on mold temperature field were discussed.

  还讨论了拉坯速度和冷却水流量对结晶器温度场的影响。

• before using, it should be dried in vacuum drier at 80-90℃. control mold temperature at 60-80℃. injecting adopted low temperature, middle speed and high pressure.

  使用前在真空烘箱中80-90℃烘干8小时以上，模具温度控制在60-80℃。注射成型采用低温、高速、高压的方法。

• by use of orthogonal test design, how the injection speed, pouring temperature and mold temperature effects the casting shrinkage porosity forming is studied.

  然后，本文通过正交试验的方法研究了压射速度、浇注温度和模具预热温度对铸件缩松缩孔缺陷的影响。

• the mold temperature obviously influences the molding process, while the melt temperature influences comparatively less.

  模具温度对成型过程的影响较大，熔体温度的影响相对较小。

• the higher the pouring temperature and initial mold temperature are, the larger the plastic strain while the smaller the thermal stress is.

  浇注温度和砂型初始温度越高，热节处粘塑性应变越大，而热应力越小。

• jtl series water type mold temperature control machine is mainly applied to the mould heating and constant temperature.

  jtl系列水式模具控温机主要应用于模具的加热与恒温。

• increasing the mold temperature increases the crystallinity level.

  增加温度将增加材料的结晶度。