片语

Repair Williams Welding标签

Repair welding technology补焊工艺

repair-welding process补焊工艺

Repair Chiricahua Welding标签

Repair r welding补焊

laser repair welding激光堆焊

repair by welding焊接修补

英汉例句

• the causes of resulting in the cracks are discussed and the proper techniques of repair welding the cracks are presented in this paper.

  本文就裂纹产生的原因和如何正确安排焊补工艺进行讨论。

• copper nickel, good machinabilitybad crack resistance. repair welding of sand holegray cast iron machined surface subject to no load.

  镍铜，易加工，但抗裂性较差。不受力的灰铸铁加工面及砂眼补焊。

• iron nickel high strength and excellent ductility. repair welding of important gray cast iron and nodular cast iron such as cylinder cap.

  镍铁，强度高、塑性好。重要灰铸铁及球铁焊补用，如汽缸盖。

• the air hole, inclusion and crack of cast steel surface can be repaired by suitable repair welding technology to get low stress, non-crackle effect.

  铸钢表面的气孔、夹渣、裂纹等缺陷可以采取适当的焊补工艺进行焊补，焊后低应力、无裂纹、效果佳。

• this paper introduces the repair welding procedure for repairing an alumal casting piece of an oil pump cylinder, this method cove…

  介绍了对油泵机缸体铝锰合金铸造件缺陷补焊修复的技术工艺，且弥补了若采用交流氩弧焊和气焊施焊时存在的不足。

• for repair welding of thin-wall weldment and working side of grey cast iron.

  用于球墨铸铁、高强度铸铁件加工面和非加工面的补焊。

• by comparison with manual arc welding, it is found that the thermit welding is a efficiency, energy saving and high quality process for repair welding of steel ingot die.

  根据对比铝热焊与手弧焊修复工艺，阐明了用铝热焊修复钢锭模是一种高效、节能、焊接质量好的新方法。

• the repair welding technology and inspecting method after welding are mainly discussed.

  重点讨论了补焊工艺及焊后检查方法。

• the invention realizes preheating before repair welding, and the strength of a repair welding joint is more than that of the deposited metals.

  本发明实现了补焊前的预热，补焊接头强度大于熔敷金属自身的强度。

• repair welding technology of allocating convex for dry gas seal in barrel type centrifugal compressor caused by operation fault is introduced.

  介绍了筒型离心式压缩机干气密封凸台由于操作上造成的缺陷，从而进行的补焊工艺。

• copper nickel good machinability and bad crack resistance. repair welding of sand hole and gray cast iron machined surface subject to no load.

  镍铜，易加工，但抗裂性较差。不受力的灰铸铁加工面及砂眼补焊。

• this paper introduces the repair welding procedure for repairing an alumal casting piece of an oil pump cylinder, this method covers the shortages of ac argon arc weld and gas welding.

  介绍了对油泵机缸体铝锰合金铸造件缺陷补焊修复的技术工艺，且弥补了若采用交流氩弧焊和气焊施焊时存在的不足。

• for repair welding of the working side and non-working side of high-strength cast iron and nodular cast iron .

  用于球墨铸铁、高强度铸铁件加工面和非加工面的补焊。

• pure nickel, excellent general properties. used to weld thin cast iron part repair welding machined surface, such as guided way of machine tool.

  纯镍，综合性能好。铸铁薄件及加工面补焊用，如机床导卫。

• a new procedure for repair welding of white cast iron roller is presented and analysis is carried out to the results. the procedure developed is easy , simple, low cost and with better result.

  介绍了白口铸铁轧辊焊接修复新工艺，并对其结果进行了分析。此工艺简便易行，耗费低廉，效果良好。

• detailed description is done on repair welding technology.

  对补焊工艺作了详细说明。

• this paper deals with the procedures, steps and precautions for repair welding of the bucket rod and the rack.

  文章介绍了斗桿、齿条焊修的程序、步骤和注意事项。

• copper nickel, good machinability bad crack resistance. repair welding of shole gray cast iron machined surface subject to no load.

  镍铜，易加工，但抗裂性较差。不受力的灰铸铁加工面及砂眼补焊。

• the repair welding of ta15 titanium alloy with flux is a mending method which can obtain high quality repairing bead.

  采用活性剂对钛合金可以进行多次补焊并能够获得高质量焊缝。

• so with the development of chinese aviation industry, advanced repair welding technology of ni-base superalloy blends will have tremendous application potentials.

  随着国内航空业的飞速发展，镍基高温合金叶片的先进焊接修复技术有着非常广阔的应用前景。

• at present, it's widely used in the production of steel made furniture, stainless products, theft-proof door, kitchen fitting ad repair welding of wire lath .

  目前广泛用于钢制家具，不锈钢制品，防盗门生产，厨房设备及钢丝网片补焊等。

• the old roller machine to use for half a year would need to open the repair, replacement or repair welding roller body.

  而旧型对辊机使用半年就需拆开大修、更换辊体或进行补焊。

• a new procedure for repair welding of white cast iron roller is presented and analysis is carried out to the results.

  介绍了白口铸铁轧辊焊接修复新工艺，并对其结果进行了分析。

• the selections of repair welding technology are compared, and the repair welding technology using handwork gas tungsten arc welding is detailed. the result with good effect is got.

  对补焊工艺方法的选择作了比较，具体阐明了采用手工钨极氩弧焊的补焊工艺方法，实践证明，效果良好。

• when the ambient temperature is lower than 0℃ and there is no any preheating available, the welding or repair welding shall not be performed for the tube.

  管子焊接过程中，焊接环境温度低于0℃时，没有预热措施，不得进行焊接。

• repair measures of large reducer with housing cracking are introduced by examples. analysis is carried out on weldability. detailed description is done on repair welding technology.

  结合实例介绍了箱体断裂的大型减速机的修复措施。对可焊性进行了分析；对补焊工艺作了详细说明。