It was observed with the MM-200 wear trial machine that carbon fiber content and trial conditions affected the tribological properties and wear mechanism with scan electron microscope.
在MM- 2 0 0型磨损试验机上考察了碳纤维含量和试验条件对其摩擦性能的影响,并利用扫描电子显微镜对其摩擦性能和磨损机制进行了考察。
The flexural strength of carbon fiber reinforced Polytetrafluoroethylene(CF/PTFE) composite increases with the increase of carbon fiber content both in modified and unmodified CF/PTFE composite.
以碳纤维增强聚四氟乙烯(CF/PTFE)复合材料弯曲强度试验结果作为依据,开展CF/PTFE复合材料界面应力的研究工作。
The influence of carbon fiber content on the properties and microstructure of the C/MC composite was studied.
研究了不同纤维含量对复合材料性能的影响。