片语

Conversion Coating Colorless转化膜无色

cerium salt conversion coating铈盐转化膜

chemical conversion coating detail化学变化保护层

chemical conversion coatingconversion coating化学氧化膜

REM conversion coating稀土转化膜

phosphate chemical conversion coating磷酸盐化学转化膜

Phosphate conversion coating磷酸盐处理

Chemical Conversion Coating化学处理膜；[化工] 化学转变护膜；[冶] 化学转化镀层

phytic acid conversion coating植酸转化膜

英汉例句

• This paper introduces the conversion coating with rust, stable rust paint, permeable paint with rust and functional mechanism, with rust paint basic scope of application and its development trend.

  本文介绍了转化型带锈涂料、稳定型带锈涂料、渗透型带锈涂料以及功能型带锈涂料基本的作用机理、适用范围及其发展趋势。

• The results show that corrosion resistance of the stannate conversion coating pretreated as following process: acid pickled by phosphate first, then alkaline pickled by s...

  结果表明：先用磷酸酸洗，再用氢氧化钠、磷酸三钠、碳酸钠溶液堿洗的预处理方案得到的转化膜耐腐蚀性能最优。

• Chromate conversion coating resulting in the formation of a passivating film.

  铬酸盐转化镀层导致形成钝化膜。只能使用三价铬。

• HY-200 process procedure for colour chemical conversion coating of al and its alloys parts and the test method for quality control are introduced in this paper.

  本文介绍了对铝及铝合金零件进行彩色化学转化处理的HY—200法的工艺及质量控制的试验方法。

• A conversion coating formed on magnesium alloy AM60 with a chromate-free bath mainly composed of silicate and tungstate is studied.

  研究了以硅酸盐和钨酸盐为主的无铬化学处理液在镁合金上所形成的转化膜。

• Abstr: Phosphate conversion coating was prepared on magnesium alloy, and it was sealing treated in sodium silicate solution.

  文章摘要：在镁合金上制备磷酸盐转化膜，并进一步用硅酸钠溶液对其进行封闭处理。

• The rare earth conversion coating technology of magnesium alloys has been developing as an environmental-friendly surface treatment technology for magnesium alloys.

  镁合金稀土转化膜技术是一种环保型镁合金表面处理新技术。

• It is shown that a chromate conversion coating needs to be used together with the non -chromate primer to meet the corrosion protective requirements.

  试验结果表明：非铬涂层需配以含铬的转化涂层才能够满足防腐性能的要求。

• A golden yellow coating was obtained by immersion process on LY12 aluminum alloy surface. The process of cerium conversion coating at normal temperature was developed.

  利用浸渍法在LY 12铝合金表面获得了金黄色的铈转化膜，确定了常温稀土(铈)化学转化膜成膜工艺。

• Cerium-based conversion coating was successfully deposited on corrosion-resisting aluminium alloy LF21 in cerium containing solution using electrolysis method.

  研究了一种通过电解沉积方法在防锈铝lf21表面上生成铈盐转化膜的工艺。

• The cerium conversion coating, which was prepared properly, would provide a better protection a-gainst corrosion for zinc and galvanized steel than the chromate conversion coating did.

  在一定条件下，铈转化膜对锌和镀锌钢的肪蚀效果优于铬酸盐转化膜。

• After sealing treatment, the surface morphology of phosphate conversion coating was improved, the corrosion potential shift positively and the corrosion resistance was enhanced.

  经封闭后，膜层的表面形貌有所改善，并且自腐蚀电位正移，耐蚀性得到提高。