英语释义

1. decarbonize

片语

malleablizing脱碳；可锻化处理

decarburization speed脱碳速度

acuum decarburization真空脱碳

decarburization process脱碳法

decarburization layer脱碳层

decarburization tendency脱碳倾向

Decarburization Trend脱碳倾向

decarburization time脱碳时间

Hydrocyclone decarburization旋流脱碳

decarburization reaction脱炭反应

英汉例句

• For grade 1, no complete decarburization shall be present. The depth of partial decarburization at any point on the periphery shall not exceed the value in table 1.

  对于等级1，没有完整的脱碳。外围任何点的部分脱碳深度不得超过表1中的数值。

• It analyzed main factors of arising spectrum analysis error which including specimen decarburization layer depth, surface roughness, describing, etc.

  分析了引起光谱分析误差的主要因素，如试样脱碳层深度、表面粗糙度、描迹等。

• There is no central segregation or decarburization and defects on the surface.

  无明显中心偏析、表面脱碳和缺陷。

• The result shows that the decarburization depth increases with the increase in temperature and holding time for the two steels.

  结果表明，两种弹簧钢的脱碳深度随提高加热温度和增加加热时间增大。

• The results show that both are caused by decarburization in heat tret - ment.

  结果表明，两者均为热处理脱碳所引起。

• The effect of rare-earth elements to prevent oxidation and decarburization in heat treating salt bathshas been discussed.

  本文就稀土对盐浴防氧化脱碳的作用进行了研究。

• It was observed that the decarburization reaction period in the RH could be classified into three stages in terms of the apparent reaction rate constants.

  据实测结果，RH炉内脱碳反应期可根据其表现反应速率常数划分为三个阶段。

• The effects of various factors on decarburization of high speed tool steel annealed in bogie hearth electric furnace were investigated in this paper.

  研究了高速钢轧材在台车式电阻炉中退火加热过程中，各因素对脱碳的影响。

• The changings of decarburization thickness were investigated by metallographic method. Then verified the accuracy of experimental datas in theory, and analyzed the protective mechanism of coating.

  应用金相法考察了试样脱碳层深度的变化，从理论上初步验证了实验数据的準确性，并合理地分析了涂料的保护机理。

• The causes of decarburization in the sintering of ferrous products using dissociated ammonia as atmosphere are analysed and some methods and routes to control decarburization are discussed.

  对铁基制品采用分解氨作烧结气氛时的脱碳原因进行了分析，探讨了几种控制脱碳的方法及途径。

• When the oxygen fuel ratio is too high, particle decarburization and binder phase nonuniform contract in the cooling process are the determining factors to the coating structure and properties.

  氧燃比过高，粒子脱碳和黏结相在冷却过程中收缩不均匀是影响涂层结构和性能的决定因素。

• The decarburization rate in bath is proportional to the intensity of oxygen supply and the utilization ratio of oxygen depends on the oxygen pressure.

  在高碳范围内熔池脱碳反应速度与供氧强度和氧气利用率成正比。而提高吹氧压力可以提高氧气利用率。

• The results show that the steel with 0.60%c possesses higher strength and hardness but lower plasticity, toughness and higher decarburization tendency.

  结果表明碳、硅可提高强度、硬度。但含0.60%C的钢塑性、韧性较低，脱碳倾向也大。

• Finally, both desulfurization and decarburization efficiency are as high as 99%. In comparison with other methods of desulfurization, this pr...

  工艺的脱硫效率和脱碳效率均能达到99%，将脱硫和制砖结为一体，具有极高的应用价值和环境效益。

• There is tight( or thin and highly adherent ) scale and decarburization , at least in certain areas .

  部件上有密布（稀疏但附着力很强）鳞片和脱碳痕迹，至少在部分区域如此。

• The invention also discloses a formula and a preparation method of the decarburization cleaner.

  本发明亦公开了脱碳清洗剂的配方和制备方法。

• The decarburization rate in bath was proportional to the intensity of oxygen supply and the utilization ratio of oxygen was enhanced with the oxygen pressure rising.

  在高碳范围内熔池脱碳反应速度与供氧强度和氧气利用率成正比，而提高吹氧压力可以提高氧气利用率。

• A new dynamic mathematical model to represent the processes of decarburization and degassing in RH vacuum refining units were developed.

  建立了描述RH真空精炼装置内钢液动态脱碳(脱气)模型。