• a flexible epoxy acrylate resin prepolymer was prepared.

  制得柔性环氧丙烯酸酯预聚体。

• these dispersions can be used as waterborne ultraviolet-curable coatings, the abrasion and flexibility of their film are better than that of epoxy acrylate coatings, but the hardness decrease little.

  这种分散体系可作为一种紫外光固化水性涂料，其涂膜的耐磨性、柔韧性都比环氧丙烯酸酯涂膜增强，而硬度变化不大。

• the title photosensitive phenolic epoxy acrylate resin has been prepared based on acrylic acid and f-44 epoxy resin as basic materials, which contains epoxy as well as acrylic groups.

  本文以丙烯酸和f-44环氧树脂为原料，合成了一种既含有环氧基又含有丙烯酸基的光敏酚醛环氧丙烯酸酯树脂。

• through vulcanization curves evaluation ammonium benzoate was selected as the vulcanizing agent of epoxy acrylate rubber (eacm).

  通过硫化曲线评定，选用苯甲酸铵作硫化剂对环氧型丙烯酸酯橡胶低温胶进行硫化。

• an uv-curing epoxy acrylate resin coatings has been prepared. the curing time, pencil hardness, adhesion, flexibility, abrasion and chemical resistance are tested, and shows a predicted result.

  合成了涂料用紫外光固化环氧丙烯酸酯树脂，并对其固化时间、铅笔硬度、附着力、柔韧性、耐磨性及耐化学品性进行测试，获得了预期的效果。

• uv-curing epoxy acrylate abrasion resistant coatings was prepared by esterification of epoxy resin e51 and e44 with acrylic acid.

  以e51和e44环氧树脂和丙烯酸为原料，制备了uv固化环氧丙烯酸酯耐磨涂料。

• at the same time, the structure of epoxy resin and epoxy acrylate resin were examined by ir.

  并用ir对环氧树脂与环氧丙烯酸树脂的结构进行了表征。

• bisphenol-s epoxy acrylate resin was synthesized with quaternary ammonium salt or tertiary amines as catalyst.

  本文用季铵盐，叔胺为催化剂合成了丙烯酸双酚-s环氧酯。

• when the mole ratio of hydroxyl of maleic anhydride and epoxy acrylate is 0.8, the formulated ink based on the modified product shows good resistance to acid, alkali, and solvent.

  当马来酸酐与环氧丙烯酸酯的羟基当量比为0。8时，以其改性产物配制的油墨具有良好的耐酸、耐堿和耐溶剂性。

• based on the principle of hlb, a scheme of epoxy acrylate modified with maleic anhydride was designed, and carboxylated acrylate epoxy with good water dispersity was synthesized successfully.

  根据亲水亲油平衡值（hlb）设计了以马来酸酐改性环氧丙烯酸酯的方案，合成了具有良好水分散性的羧基化环氧丙烯酸酯树脂。

• properties of epoxy acrylate synthesized from epoxy resin by modification and esterification;

  合成了既有环氧基团又含不饱和双键的环氧丙烯酸单酯树脂。

• epoxy acrylate (ea) resin is an important photosensitive resin, in which bisphenolic epoxide was most widely used in the field of uv curing coating.

  环氧丙烯酸（ea）树脂在辐射固化领域中是一种重要的感光树脂，其中双酚a型环氧树脂的应用最为广泛。

• the epoxy acrylate was synthesized with different amounts of inhibitor, feed ratios and feeding modes.

  在不同阻聚剂用量、投料比、投料方式等条件下合成环氧丙烯酸酯。

• epoxy acrylate was synthesised by reacting epoxy resin with acrylic acid.

  用丙烯酸和环氧树脂合成了丙烯酸环氧酯。

• it was showed from the experiment that: epoxy acrylate oligomers had good adhesiveness and dye wettability, high luster and rigidity, and excellent solvent resistance;

  通过实验可以看出：环氧丙烯酸酯齐聚物具有良好的附着力、颜料润湿性、高光泽、高硬度与优异的耐溶解性；

• the synthesis of epoxy acrylate type photosensitive coatings were developed by semi-ester method.

  开发了一种用半酯法合成环氧丙烯酸酯型光敏涂料的方法。

• the invention belongs to the field of synthesizing organic chemical materials and discloses modified bisphenol a epoxy acrylate and a preparation method thereof.

  本发明属于有机化学材料合成领域，公开了一种改性双酚a环氧丙烯酸酯及其制备方法。

• the basic composition of uv curable coating and effect of quality of bpa type epoxy resin on the synthesis of epoxy acrylate and the property of uv curable coat were introduced in this paper.

  介绍了紫外光（uv）固化涂料基本组成，双酚a环氧树脂质量对环氧丙烯酸酯的合成及对uv涂料性能的影响。

• water-base epoxy acrylate and polyurethane acrylate are synthesized as the oligomers of uv curing coating for wood floor.

  合成了水性环氧丙烯酸酯和水性聚氨酯丙烯酸酯，作为uv固化木地板涂料的预聚物。