片语

notch effect sensitivity test缺口敏感试验

fatigue notch sensitivity疲劳缺口灵敏度

notch h sensitivity切口灵敏度

notch sensitivity factor缺口敏感性系数

notch sensitivity ratio凹口敏感比

notch sensitivity test缺口脆性试验

英汉例句

• the tests shown that the creep ductility were increased and the notch sensitivity of alloy were improved through multiple aging treatments.

  试验指出，通过多次时效处理可以提高合金的蠕变延性，改善合金的缺口敏感性。

• the notch sensitivity of az31 magnesium alloy was studied.

  研究了az31镁合金板材的缺口敏感性。

• the influence of stress rupture notch sensitivity on crack growth rates have been investigated in gh36 iron-base superalloy discs.

  研究了gh36合金持久缺口敏感性对裂纹扩展速率的影响。

• a notch sensitivity factor was derived in order to judge the stress concentration sensitivity of al li based alloys.

  建立了评价铝锂合金应力集中敏感性的缺口敏感因子。

• the results show that the crack propagation work of v-notched specimen can well reflect the notch sensitivity of the tested steels.

  结果表明：v型缺口试样的裂纹扩展功能较好地反映材料的缺口敏感性。

• the expression of the notch strength and the notch sensitivity factor are correspondingly verified by test data.

  切口强度和切口敏感度因子的估算公式均用实验作出检验。

• the result shows that the objection left during the machining of the axle lead to the notch sensitivity of the axle.

  结果表明，长销轴表面加工时留下的切削缺陷，使销轴形成缺口敏感；

• compared with the forging die steel, casting forging die steel although toughness is low, but high strength, red hardness is good, with low notch sensitivity and high resistance to thermal fatigue.

  与锻造模具钢相比，铸造热锻模具钢虽然韧性低，但强度高、红硬性好，具有较低的缺口敏感性和较高的抗热疲劳性。

• analysis and observation under electron microscope indicated that it seems to attribute the notch sensitivity of the alloy to the film-like boride along the grain boundaries substantially.

  电子显微镜观察与分析表明，晶界上的薄膜状硼化物是导致合金缺口敏感的主要原因。

• effect of microstructure on notch sensitivity of low-carbon bainitic steel is investigated by using mechanics knowledge and transmission electron microscope.

  通过光学、电子金相分析，并应用力学知识，探讨了组织因素对缺口敏感性的影响。

• the notch sensitivity of hsc and steel fiber reinforced hsc and the strain field of hsc reinforced with steel fibers ahead of the crack tip have been analyzed.

  分析了钢纤维高强混凝土和普通高强混凝土的缺口敏感性以及钢纤维对高强混凝土裂缝前缘应变场分布的影响。