• the dependences of seepage velocity and bending strength on agglomerant content, forming pressure, particle diameter of the aggregate, soaking time, firing temperature and so on were discussed.

  分别从外加粘结剂百分数、成型压力、骨料粒径、保温时间、烧成温度等因素对渗水砖的渗水速度和强度的影响进行了探讨。

• the factors which affect the firing temperature of the glaze were discussed, and the opacifying mechanism of glaze was also approached.

  探讨了影响釉烧成温度的诸因素及釉的乳浊机理。

• it has a low firing temperature and may be used for the termination electrode of mlci, wwci and mlcc. results indicate that technical and process properties of the silver termination paste are good.

  实验结果表明：本浆各项技术指标、工艺性能良好，完全能满足多（叠）层片式电感器（mlci）生产线的使用要求，并可用于制作绕线电感器（wwci）与片式电容器（mlcc）的端电极。

• the main factors for preparation were studied, including the proportion of raw materials, firing temperature and time, reducing atmosphere, flux and so on.

  主要研究了原料配比、烧结温度、保温时间、还原气氛、助熔剂等对材料发光性能的影响。

• the analysis of the properties and microstructure show that the content of red mud and firing temperature are the main factors that influence the microstructure and performances of the materials.

  本文以烧结法赤泥为主要原料制备了多孔陶瓷滤球，研究了赤泥添加量、烧成温度等对样品的烧成温度范围、显气孔率、压碎强度、耐酸耐堿性、显微结构等的影响。

• color results will vary according to glaze composition, firing temperature and kiln atmosphere.

  唯基础釉的组成物料、烧温度、氧化或还原均会影响烧成的颜色。

• the best peak firing temperature was existed, which was between the softening temperature and the peak crystallization temperature, and near the incipient crystallization temperature of the glass.

  电阻浆料存在最佳峰值烧成温度。 理论分析表明，最佳峰值烧成温度应在软化点与峰值析晶温度之间，靠近起始析晶温度。

• in this paper, the varying laws of the properties of cordierite-containing honeycombedceramic were studied when firing temperature and hold time were changed.

  本文研究了堇青石蜂窝陶瓷的性能随烧成温度和保温时间变化的规律；

• as substitution of diopside for talc, the body has lower firing temperature and widening sintering range. the property of diopside porcelain is in keeping with standard of high frequence dielectric.

  用透辉石代替滑石时，透辉石瓷有较低的烧成温度和较宽的烧结范围，其性能符合高频电介质标準的要求。

• then the firing temperature is higher than when firing tiles 1200 ℃, it will decay of radium element.

  那么在烧制瓷砖时烧制温度高于1200℃，镭元素就会衰变。

• effects of micro-powder and firing temperature on microstructure and properties of corundum-mullite materials;

  首先，研究了红柱石的粒度和加入量对莫来石-刚玉材料性能的影响。

• the high temperature foamed ceramic produced has low firing temperature, short duration of firing, wide range of firing temperature and easily control production.

  研制的高温发泡陶瓷具有烧成温度低、烧成时间短、烧成温度范围宽、易于生产控制的特点。

• the results show that appropriate firing temperature is 1400℃, and additional zircon or bauxite can improve thermal shock of the products. so they might be a good kiln furniture material.

  结果表明：合适的制品烧成温度为1400℃，添加锆英砂或焦宝石可以提高其热稳定性，可望成为较好的窑具材料。

• firing temperature for the production of special circuits in the internal connection and end lead, ptc thermistors, and semiconductor ceramic device electrodes.

  适用于中温烧成制作特种电路的内部连线及端头引出线，ptc热敏电阻及半导体陶瓷器件电极等。

• porcelain:the quality of porcelain has direct relationship with the service life of sits implement. if the firing temperature is higher, the quality of porcelain will be better.

  瓷质：瓷质的好坏和马桶的寿命有直接的关系，烧成温度越高，瓷质越好。

• the color glaze of low firing temperature and low expansion coefficient, to match the glaze tile made from common clay, was prepared in lead borosilicate system.

  采用铅硼硅系统，研制出具有低烧成温度、低热膨胀系数的色釉，用作粘土釉面瓦釉料，其外观、物理、化学性能均能满足质量要求。