英汉例句

• The Influence of quenching temperature on wear resistance of high boron casting steel was investigated.

  研究了不同的淬火温度对高硼铸钢沖击耐磨性的影响。

• The effects of polymer molecular weight and quenching temperature on the porous structure are also discussed.

  讨论了聚合物分子量及淬冷温度对成膜孔结构的影响。

• It is shown by the results that the morphology of microstructure is dependent on the interrupted quenching temperature strongly.

  结果表明，微观组织形态取决于水淬终止温度。

• The Influence of quenching temperature and tempering temperature on mechanical properties and microstructure of ZG310-510 cast steel was studied.

  研究了淬火温度和回火温度对ZG310- 510铸钢组织和力学性能的影响。

• The main cause of the cracking is that the quenching temperature is too high.

  结果表明，钢球开裂为淬火开裂，淬火温度过高是导致淬火钢球开裂的主要原因。

• Hardening depth related to the technical parameters and the quenching temperature field is an important target by plasma surface quenching.

  硬化层深度是等离子弧表面淬火效果的重要指标之一，而硬化层深度与工艺参数、淬火过程中温度场的变化密切相关。

• The influences of isothermal quenching temperature on the retained austenite and mechanical properties of ADI were studied.

  研究了等温淬火温度对ADI中残余奥氏体及其力学性能的影响。

• The results show with increasing quenching temperature the brittle temperature of the steel tempered at low temperature brittle temperature moves upwards.

  结果表明：随淬火温度提高，低温回火脆性区向高温区漂移。

• The influences of quenching temperature on mechanical properties of the pipeline steel were investigated by means of microscopic analysis and mechanical property test.

  采用力学性能测试、显微组织分析等方法研究了终冷温度对双相大变形管线钢的力学性能的影响。

• The results showed that the austenite recrystallization occurs in a temperature range biger than thenormal quenching temperature and there is an optimum temperature range for the grain refining.

  结果表明，奥氏体的再结晶发生在钢的正常淬火温度以上的一个温度范围，并在该范围内存在晶粒细化效果最佳的温度区域；

• The hardness variation of D2 steel under different quenching temperature and the influence of subzero treatment on hardness of D2 steel were studied, and its microstructure was analyzed as well.

  研究了D2钢在不同温度淬火后的硬度变化，以及深冷处理对其硬度的影响，并对其显微组织进行了分析。

• The content and stability of retained austenite is higher after more Mn is added, and also the strength is higher with preferable elongation when the appropriate quenching temperature is chose.

  锰含量提高并选取合适的淬火温度后，残余奥氏体含量及稳定性提高，抗拉强度显着提升的同时保持了较高的伸长率。

• The influences of different microstructure, silicon content, quenching temperature and cooling rate of the SiCr white cast iron on its abrasive wear performance were investigated.

  研究了硅铬白口铸铁不同组织、不同含硅量、不同淬火加热温度及冷却速度对其耐磨粒磨损性能的影响。

• The embrittlement of the welds increases with the increase of quenching temperature of PWHT.

  淬火温度越高，焊缝脆化越严重；

• On the other hand, the parts might become more brittle at higher quenching temperature because of the coarse martensite.

  若淬火温度较高，由于粗大马氏体的存在，脆性很大；