英汉例句

• the result showed that impact strength of the blending system increased, while tensile strength, flexural strength and flexural modulus decreased with the addition of impact modifier acr;

  酯交换抑制剂的加入，降低了共混体系的力学性能，适当的酯交换反应有利于共混体系力学性能的提高；

• results showed that as the hardness of modified epdm increased the brittle-ductile transition moved to high rubber contents and the flexural modulus increased profoundly, however.

  结果表明：随着epdm硬度的增加，共混物不仅韧性提高，弯曲模量也大幅度上升。

• when carbonization temperature is below 600℃, volume density and flexural modulus decreases with the temperature rising.

  炭化温度低于600℃时，复合材料的体积密度和弯曲模量随炭化温度的升高而下降；

• flexural strength and modulus of super-hybrid composite can be improved greatly by the better interfacial control. and the increasing rate of flexural modulus is more than that of flexural strength.

  通过良好的界面控制，可显着提高复合材料的弯曲强度和弯曲模量，模量的提高比强度的提高幅度更大。

• experimental results showed that the increase of the addition amount of the sand could significantly raise both the flexural strength and the flexural modulus of the composites.

  实验结果表明，随着砂料含量的增加，材料的弯曲强度和弯曲模量也相应增加；

• flexural strength and flexural modulus of cf/bpr composites increase when the surface of carbon fiber is treated, but impact strength of cf/bpr composites decreases slightly.

  bpr复合材料弯曲强度和弯曲模量因碳纤维的表面处理而提高，但沖击强度却略有下降。

• experimental results show that the flexural modulus increases with the increases of the fibre content and length.

  实验表明，随着纤维含有量和纤维长度的增加，材料弯曲模量呈递增趋势。

• the addition of ommt improved the tensile strength, flexural strength and flexural modulus of the alloy, however, the impact strength decreased to a certain extent.

  结果表明，om mt的添加可以提高体系的拉伸强度、弯曲强度和弯曲模量，但沖击强度会有某种程度的下降；

• higher ethylene content, mass fraction of xylene soluble part in copolymer and higher intrinsic viscosity of this part had negative effects on tensile strength and flexural modulus of copolymer.

  提高共聚物中的乙烯含量、二甲苯可溶物含量或二甲苯可溶物特性粘数，共聚物的拉伸强度和弯曲性能降低；

• the results showed that the tensile strength, flexural strength and flexural modulus increased obviously with increase of amount of mica.

  结果表明，复合材料的拉伸强度、曲强度和弯曲模量随着云母用量的增加而提高。

• the flexural strength and flexural modulus decreased with the increasing amount of abs.

  合金的弯曲强度和弯曲模量都随着合金中abs用量的升高而下降。

• improves polypropylene's m. f. i, flexural modulus and impact strength.

  改进聚丙烯的m.f.i、弯曲模量和沖击强度等指标。