片语

entrapped slag inclusion卷渣

slag inclusion elds焊缝中的夹渣

interpass slag inclusion焊道内夹渣

endogenous slag inclusion本智周万物夹渣

concrete slag inclusion混凝土夹渣

oxidation slag inclusion氧化物夹渣

cinder inclusion夹渣；包渣

slag inclusion entrapped slag夹渣

Isolated Slag Inclusion单个的夹渣

Slag inclusion welds焊缝中的夹渣

slag blister渣眼；夹渣

英汉例句

• the result shows that slag inclusion in continuous casting billet cause the infolding, and the way to reduce infolding by improving the quality of billet is suggested.

  结果表明，连铸坯中心存在大量夹渣物，致使在穿孔轧制过程中形成内折缺陷。提出了改进措施。

• by using this process to repair castings, there is no obvious separating line, no slag inclusion and gas hole between the welding zone and base metal.

  用此工艺焊补铸件，焊补区域与基体间没有明显的熔合线，无渣孔、气孔等缺陷。

• reaction of rare earth with oxygen and sulfur can improve the shape of slag inclusion while purifying surfacing.

  稀土钇与氧、硫结合在凈化堆敷金属的同时，改善了堆敷金属中夹渣物的形态。

• stomatal, dispersed shrinkage, shrinkage cavity, sonim and slag inclusion belong to this kind of defect.

  属于这种类型的缺陷有气孔、缩松、缩孔、夹砂、夹渣等。

• the reasons causing sand inclusion and slag inclusion are: ( 1 ) gaps between mould and core prints or cods too small;

  前言： 湿砂型铸铁件产生砂孔和渣孔缺陷的主要原因是：（1）芯头或砂台的间隙偏小；

• the results showed that the oxidation slag inclusion and central porosity in the raw material were the direct reasons which the forging cracking.

  结果表明，锻坯原材料中存在的中心疏松和氧化物夹渣等低倍缺陷是导致锻件开裂的主要原因。

• the use of ceramic foam filter makes slag inclusion decrease greatly. it is an efficient way to obtain double corona stationary blades with little or no slag inclusion.

  使用泡沫陶瓷过滤器使除渣有显着效果，是获得少、无夹渣带冠导叶的一种有效途径。

• based on the analysis of site welding, the main welding defects are lack penetration, lack fusion, slag inclusion and porosity.

  从现场施工情况分析，焊接的内部缺陷主要有未焊透、未熔合、夹渣和气孔等几种。

• the results show that the porosity is major factor of affecting the mechanical properties, while the slag inclusion is minor factor;

  结果表明：缩松是影响轮辋性能的主要因素，而夹渣对性能的影响相对较小；