英语释义

1. a mineral consisting of magnesian olivine specifically magnesium silicate Mg2SiO4 constituting the essential component of some refractories

片语

forsterite e镁橄榄石

forsterite ceramic[陶瓷]

forsterite twin涵义镁橄榄石连晶

forsterite products镁橄榄石制品

forsterite pelletization橄榄石球团

synthetic forsterite合成镁橄榄石

Forsterite sand镁橄榄石砂

forsterite whiteware镁橄榄石白坯陶瓷器皿

forsterite refractory镁橄榄石耐火材料

英汉例句

• using natural forsterite and magnesite clinker as raw materials, the forsterite refractories with micropore and high strength has been prepared by foaming method.

  以镁橄榄石和镁砂为主要原料，粘土为结合剂，利用泡沫法制备了微孔、高强度的镁橄榄石制品。

• the forsterite ore deposit in yichang of hubei province, being one of the limited large ore deposits across the mainland china, is used to produce molding sand.

  宜昌镁橄榄石矿，是我国为数不多的大型矿床之一，用其矿石生产的镁橄缆石型砂。

• the other for high mn steel castings, consists mainly of forsterite powder with a few addition of fibre-like mineral both additions are used for improving permeability.

  另一种以镁橄榄石粉为耐火材料，加少量纤维状矿物，改善透气性，用于高锰钢铸件。

• when the temperature reaches 650 ℃, the crystallinity of forsterite is improved, then another new mineral phase enstatite appears.

  温度升高到65 0℃时，镁橄榄石结晶度增高，并出现顽火辉石新物相；

• there is a good prospect to develop forsterite sand and forsterite brick in zhubu and heinipo, develop water soluble fertilizer with magnesite byproduct in baitongchang.

  白泥湾白铜厂为含镍蛇纹菱镁片巖。朱布、黑泥坡开发镁橄榄石砂、镁橄榄石砖与白铜厂开发水溶性农肥并副产菱镁矿均具良好的开发前景。

• it is also demonstrated that, when heated to 825℃, the structure was destroyed and forsterite phase formed.

  矿物加热到825℃时，结构开始破坏并出现镁橄榄石相。

• the results show that when heated up to 700℃, the serpentine cat's eye completely dehydrates and partly transforms into crystalline forsterite and non-crystalline enstatite.

  结果表明：加热到700℃时，蛇纹石猫眼完全脱羟，同时部分转变为晶质镁橄榄石和非晶质顽火辉石。

• tests results showed that: the addition of forsterite powder is helpful to improve green ball quality, however the addition of forsterite powder had little influence on technic parameters of balling.

  试验研究表明：镁橄榄石粉的添加对生球质量的提高可以起到一定程度的促进作用，而且对造球工艺参数不会造成影响；

• the dry vibrating material is prepared with magnesite or forsterite in 85-97 wt% and sodium metasilicate in 3-15 wt%, and through mixing, vibration forming, stoving at 100-400 deg. c and demolding.

  其技术方案是：按重量百 分含量将85～97％的镁砂或镁橄榄石与3～15％的偏硅酸钠混合，搅拌均匀后采用胎膜振动成型，在100～400℃烘烤，脱模得到中间包干式振动料。

• properties and its production technology of forsterite were presented.

  介绍了镁橄榄石矿物性质及其生产工艺。