片语

fracture appearance transition temperature脆性转变温度

Percent shear fracture appearance剪切面积百分比

fibre fracture appearance纤维断口形貌

fracture appearance parameter断口形貌参数

fracture surface appearance破坏形貌

fracture e appearance断口外观

fracture micro-appearance断口微观形貌

fracture appearance analysis断口形貌分析

英汉例句

• the relationship between fracture appearance and mechanical properties was analyzed. the microstructure of the composites was observed by environment scanning electron microscope (esem).

  利用环境扫描电镜（esem）观察了微观组织、断口形貌， 并分析了它们与力学性能之间的关系；

• the fracture appearance of both materials belongs to ductile fracture.

  两种材料在高温下的断口形貌均表现为韧性断裂。

• the paper introduces fracture appearance transition character of turbine high and middle pressure rotor made metal material.

  介绍汽轮机高中压转子金属材料的脆性转变特性。

• percent shear fracture appearance is an important factor to evaluate neutron irradiation embrittlement of nuclear pressure vessel steel.

  在核压力容器钢的中子辐照脆化评价中，断口剪切面积百分比是一个重要的参数。

• the analysis of materials and fracture appearance shows that the cracks on the hanger of ropeway are caused by fatigue failure.

  通过材料性能检测、金相组织检验和断口形貌分析，确定了索道吊架失效是疲劳破坏。

• analysis on metallography, macro and fracture appearance were carried out on broken link in motorbike engine.

  对断裂的摩托车发动机连桿进行宏观、金相及断口分析。

• the structure, fracture appearance and eds of ccs board sample at 0℃ of handan iron and steel group co. are analyzed.

  对邯钢ccs船板钢沖击试样（0℃）进行了金相组织、沖击断口形貌及能谱分析。

• the study gained the perfect correlative parameters of electrochemistry polarization about fracture appearance transition temperature (fatt50), discussed other parameters;

  找到了与转子钢韧脆转变温度（fatt50）相关性的最佳电化学极化参数，讨论了影响fatt50的其它参数；

• sem was used to observe the fracture appearance of the specimen.

  用扫描电镜（sem ）观察了试样的断裂口形貌。

• the results show that the chemical composition, macrostructure and microstructure are normal, the fracture appearance is brittle crowbarand, and the fracture was oxygenated severely.

  分析结果表明，断裂钢轨化学成分满足标準要求，低倍组织和显微组织正常，断口呈脆性断裂解理特征，断口处氧化严重。