• as the grafting degree increase, the contact angle to water of aa-grafted hdpe powder decreases.

  随接枝率的增大，接枝hdpe与水的接触角下降，亲水性增加。

• the influences of concentration of bpo, concentration of monomer, reaction time, reaction temperature were investigated in terms of grafting degree and gel content.

  研究了单体浓度、引发剂浓度、反应时间和反应温度对接枝聚合物接枝率、凝胶率等的影响。

• tensile strength and lap shear strength increased with increasing of grafting degree due to great improvement of polarity.

  离聚体的拉伸强度、搭接剪切强度和乳化性能均随顺酐化程度的提高而改善。

• the grafting degree can reach above (1.8%).

  称量法表明接枝率可达1.8%以上。

• the grafting degree increased with increasing bpo concentration, reaction time and reaction temperature.

  接枝率随引发剂浓度、反应时间、反应温度的增加而增加；

• the results showed when the grafting degree was 15% and kaolin content was 10% , the blend system had a better tensile strength.

  结果表明在接枝度为15%、高岭土填充量为10%时，体系具有较高的拉伸强度。

• the grafting degree of the specimens that was taken from upstream and downstream reaction zone was determined by titration.

  结果表明：物料的熔融终了点和主反应区的充满度对接枝反应率有较大的影响。

• once the temperature is higher than the melt point of nipaam, the grafting degree decreases strikingly.

  提高反应温度可以显着的提高接枝程度，但是当温度高于单体熔点时，接枝程度反而大幅降低。

• the influences of monomer mass fraction, dcp mass fraction, reaction temperature and rotating velocity on grafting degree were investigated.

  研究了单体质量分数、引发剂质量分数、反应温度和转子转速对接枝聚合物接枝率的影响。

• the copolymerization was confirmed by ft infrared spectra and the grafting degree and grafting efficiency were measured by chemical titration.

  采用化学滴定法测定了反应产物的接枝率和接枝效率；

• the grafting degree increased with the increase of monomer mass fraction and dcp mass fraction.

  单体质量分数、引发剂质量分数增加，接枝率增加。