英语释义

1. tempered martensite having a granular appearance under the microscope

片语

primary sorbite初生索氏体

sorbite zone索氏体带

D-sorbitol山梨醇；山梨糖醇

sorbite rail耐磨钢轨

sorbite percentage索氏体含量

sorbite e索氏体

sorbite extraction提取法

secondary sorbite回火讼体

sorbite structure讼体组织

glucitol山梨醇；葡萄糖醇

英汉例句

• increasing the cooling rate can increase the content of sorbite and decrease the content of network cementite;

  提高冷却速度可以增加索氏体含量、降低网状渗碳体含量；

• the results indicate that, with the increase of rolling times, the grain size becomes smaller, the content of sorbite multiplicates, and the yield strength improves.

  结果表明，随轧制道次的增加，晶粒尺寸逐渐减小，索氏体的含量不断增加，屈服强度逐渐提高。

• the results show that x80 pipeline steel obtains sorbite after quenching and tempering, gets pearlite by normalizing.

  结果表明：x80钢经调质处理后得到索氏体，正火得到珠光体。

• the ginger like sorbite forming mechanism and the high wear resistance of ginger like carbide cutter blade were studied in this paper.

  本文从空间形貌上说明姜块状碳化物的形成机制，并从微观机理分析姜块状碳化物提高刀片耐磨性的原因。

• the results show that 82b wire rod brittle fracture is mainly caused by excessive inclusion, reticulate carbide, lower sorbite in the microstructure, and surface defect of wire rod.

  结果表明，82b钢盘条脆断的主要原因是夹杂物级别超标、组织中出现网状碳化物、索氏体含量偏低以及盘条表面缺陷等。

• with the decrease of finishing rolling temperature, the grain size is refined apparently and the contents of sorbite is increased.

  随着终轧温度的降低，热轧材组织得到细化，索氏体含量提高。

• the lath character of martensite in welded joint disappears, and the carbide in the tempered sorbite of the base metal will aggregate when temper temperature is above 780℃, and the hard…

  回火温度超过780℃，焊缝板条马氏体特征消失，母材回火索氏体中碳化物产生偏聚，硬度、 塑性明显降低。

• the results indicated that the tempered sorbite was the optimum microstructure, the inhomogeneous distribution of micro hardness affected markedly the finish quality of the steel surface.

  结果表明：回火索氏体是最佳的组织形态；微观硬度的不均匀性显着影响钢的表面加工质量。