片语

brush-plating coatings电刷镀层

brush the plating刷镀

electric brush-plating电刷镀

surface brush-plating表面刷镀

electro brush-plating电刷镀制备工艺

compound brush-plating复合刷镀

brush-plating technology刷镀技术

英汉例句

• According to the surface abrasion form of cast iron seal ring, the author proposed that composite brush plating can effectively repair and strengthen the mating surface of cast iron seal ring.

  根据铸铁密封环的表面磨损形式，提出采用复合刷镀技术可有效修复和强化铸铁密封环的配合面。

• The effects of C2N2H8 on the properties of copper brush plating solution and copper deposits are investigated in the present paper.

  主要就乙二胺在电刷镀铜溶液中的作用及其对镀铜层性能的影响进行了试验研究。

• Dai J, ZhuM. Technology discussion of brush plating on stainless steel shaft [J]. Mechanical design and manufacturing engineering, 2001, 30(4): 52(in Chinese).

  ? [11]戴剑， ， 朱明。电刷镀修复不锈钢转轴的工艺与探讨 [J]。机械设计与制造工程， 2001，30（4）：52。

• The process of the brush plating Ni, the microstructure and the properties of the plating layer are studied and analyzed.

  研究了电刷镀镍的工艺、镀层微观形貌与镀层性能。

• To achieve the best match, the power source controller for rub brush plating and GTAW welding has been developed on the experiment's foundation in this paper.

  为了实现摩擦电刷镀与GTAW焊接的最佳配合使用，本文在实验的基础上研制了一台GTAW焊接与摩擦电刷镀电源控制器；

• The application of brush plating on H-6000-crusher cone axis was introduced, and the process and conditions during brush plating were obtained.

  介绍了电刷镀技术在H-6000型破碎机锥形轴修复中的应用，提出了电刷镀修复H-6000型破碎机锥形轴的工艺流程及条件。

• Base on these, a composite coating containing nano-powder is prepared by brush plating in this thesis.

  基于此，本文创造性地将复合电刷镀技术和纳米粉材料有机结合，成功制备了含纳米粉复合电刷镀层。

• The field application proves that the corrosion free service life of plain rod with brush plating is more than two times as long as that of the original on...

  现场应用情况表明，采用电刷镀镀层的光桿，无腐蚀使用寿命已经达到原来的两倍以上。

• The major problems of brush plating bath and the effect of soluble and non-soluble positive pole on various brush plating baths in iron plating are discussed.

  本文研究了电刷镀铁镀液存在的主要问题，可溶性阳极和不溶性阳极对电刷镀铁不同类型镀液氧化的影响及原因。

• The microstructure of initial brush plating layer was studied along with its influencing factors as the direction of brush plating, time, voltage and temperature.

  研究了刷镀起始镀层组织及其影响因素，分析了刷镀方向、刷镀时间、刷镀电压、镀液温度对起始镀层组织的作用。

• The result shows that the nano-particle surface charge is negative and its diameter distribution is more wide in brush plating solution.

  实验结果表明纳米颗粒在镀液中荷负电，其粒径分布较广；

• An equipment for rapid die manufacture with the combination of electric arc spraying and brush plating was introduced.

  并介绍了电弧喷涂和电刷镀一体化快速模具制造设备。

• Results show that foe brush plating indium -copper alloy is able to improve frictional state of the ring and the hot spraying PTFE will deteriorate the frictional state of the ring.

  结果表明刷镀铟铜合金能够改善涨圈摩擦副的摩擦状态而热喷涂ptfe使摩擦状态恶化。

• The field application proves that the corrosion free service life of plain rod with brush plating is more than two times as long as that of the original one.

  现场应用情况表明，采用电刷镀镀层的光桿，无腐蚀使用寿命已经达到原来的两倍以上。

• In this paper the application of the brush plating technology in mending surface damage of Austenite stainless steel parts is introduced. The process and conditions of this technology are put forward.

  本文介绍了电刷镀技术在奥氏体不锈钢零部件表面损伤修复中的应用，提出了电刷镀修复奥氏体不锈钢件的工艺流程及条件。

• The ways to prevent iron brush plating solution from being oxidized during storage and working are described.

  阐述电刷镀铁液贮存期间和刷镀过程中防氧化的方法。

• Compared with brush plating Ni, brush plating Fe has more advantages as low cost and high hardness.

  刷镀铁与刷镀镍相比具有成本低、硬度高的优点。