英汉例句

• hdpe 6360m successfully produced in a hdpe slurry plant possessed superior physical properties, good processability and high environment stress cracking resistance(escr).

  在hdpe淤浆法工艺生产装置上，开发了具有优良的物理性能、加工性能和耐环境应力开裂（escr）性能的埋地排水管材专用树脂6360m。

• delamination and cause of polycarbonate(pc) thin-wall component were studied by comprehensive analysis methods and chemical stress cracking mechanism of pc delamination was found.

  应用综合分析方法研究了聚碳酸酯（pc）薄壁件分层开裂及其起因，发现了分层的化学应力开裂机制。

• authors inter-prete all experimental results of the work with the molecular mechanism of fracture behaviour of polymers and propose the mechanism of chemical stress cracking of pet-methylamine system.

  作者从高聚物断裂的微观机理解释了所有实验结果并提出pet-甲胺系统化学应力开裂机理。

• the thermal stress cracking is initiated without the use of mechanical force.

  热应力裂纹的启动没有利用机械力。

• hdpe can cause stress cracking easily with affection of environment, which limits its application in industry.

  hdpe易受环境的影响产生应力开裂，这限制了其在工业上的应用。

• as the load increased, the time growth can lead to stress cracking phenomenon.

  随着负荷加大、时间增长，可导致应力开裂现象。

• the chemical stress cracking of pet fiber-methylamine system is considered to be a fracture phenomenon of polymers.

  pet纤维-甲胺系统的化学应力开裂被归结为一种高聚物断裂破坏现象。

• highest heat and stress cracking resistance of lucky pmma grades. recommended for extrusion of sheets, pipes, and profiles.

  高耐热、耐应力开裂、用于挤出级、板材、型材、管材等用；

• a burner and water spray are arranged to cause thermal stress cracking along a cutting line extending along a continuous glass ribbon, parallel with the edge of the ribbon.

  燃烧器和喷水器布置成沿着切割线产生热应力裂纹，所述切割线沿着连续的玻璃带延伸，并平行于玻璃带的边缘。

• it showed that a fast cooling after drawing was of benefit to dimensional stability, straightness, environmental stress cracking resistance, and strength of the drawn tubes.

  拉伸时的自然冷却会产生不均匀的产品，快速水冷却拉伸工艺能显着改善管的耐环境应力开裂性，成倍提高其强度。

• in this paper was presented a study on environmental stress cracking resistence (escr)on types of hdpe 6300m and 2480, which had been used in the production of plastic pipes.

  研究了成型塑料管材的两种牌号的高密度聚乙烯（hdpe）6300m和2480的耐环境应力开裂（escr）性能。

• the sulfide stress cracking is one of the reasons of gas transmission pipeline failure.

  硫化物应力腐蚀是引起输气管道失效的主要原因之一。

• siloxane was grafted on the low density polyethylene to improve the property of the environmental stress cracking of low density polyethylene.

  研究了低密度聚乙烯接枝聚硅氧烷后的环境应力开裂性。